| 三个含4，4'-(吡啶-3，5-二基)二苯甲酸配体的锌(Ⅱ)、镍(Ⅱ)和钴(Ⅱ)配位聚合物的合成、晶体结构及催化性质 |
| Syntheses, crystal structures, and catalytic properties of three zinc(Ⅱ), nickel(Ⅱ) and cobalt(Ⅱ) coordination polymers constructed from 4, 4'-(pyridin-3, 5-diyl)dibenzoic acid |
|
| 摘要: 采用水热方法，选用4，4'-（吡啶-3，5-二基）二苯甲酸配体（H2pdba）与菲咯啉（phen）、2，2'-联吡啶（bipy）或2，2'-联咪唑（H2biim）分别与ZnCl2、NiCl2·6H2O和CoCl2·6H2O在160 ℃温度下反应，合成了2个二维层状配位聚合物{[Zn（μ3-pdba）（phen）]·H2O}n （1）和{[Ni（μ3-pdba）（bipy）]·3H2O}n （2），以及1个具有一维链结构的配位聚合物{[Co（μ3-pdba）（H2biim）（H2O）]·H2O}n （3），并对其结构和催化性质进行了研究。研究表明，在70 ℃条件下配合物1在Henry反应中显示出较好的催化活性。优化了反应参数，对反应底物范围也进行了研究。 |
| 关键词: 配位聚合物 二羧酸 催化性质 Henry反应 |
| 基金项目: |
| Abstract: Three zinc(Ⅱ), nickel(Ⅱ), and cobalt(Ⅱ) coordination polymers, namely {[Zn(μ3-pdba)(phen)]·H2O}n (1), {[Ni(μ3-pdba)(bipy)]·3H2O}n (2), and {[Co(μ3-pdba)(H2biim)(H2O)]·H2O}n (3) have been constructed hydrothermally using 4, 4'-(pyridin-3, 5-diyl)dibenzoic acid (H2pdba), 1, 10-phenanthroline (phen), 2, 2'-bipyridine (bipy), 2, 2'-biimdazole (H2biim), and zinc, nickel and cobalt chlorides at 160 ℃. The products were isolated as stable crystalline solids and were characterized by IR spectra, elemental analyses, thermogravimetric analyses, and single-crystal X-ray diffraction analyses. Single-crystal X-ray diffraction analyses reveal that the three compounds crystallize in the monoclinic system, space groups P21/c or P21/n. Compounds1 and2 show 2D networks. Compound3 discloses a 1D ladder chain structure. The catalytic activities in the Henry reaction of these compounds were investigated. Compound1 exhibited an effective catalytic activity in the Henry reaction at 70 ℃. For this reaction, various parameters were optimized, followed by the investigation of the substrate scope. |
| Keywords: coordination polymer dicarboxylic acid catalytic property Henry reaction |
| 投稿时间：2023-06-21 修订日期：2023-10-07 |
| 摘要点击次数: 1646 |
| 全文下载次数: 820 |
| 亢秀琪,王嘉浩,顾金忠.三个含4，4'-(吡啶-3，5-二基)二苯甲酸配体的锌(Ⅱ)、镍(Ⅱ)和钴(Ⅱ)配位聚合物的合成、晶体结构及催化性质[J].无机化学学报,2023,39(12):2385-2392. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: 相关附件： 20230241_Supporting_Information.doc |
|
|
|
|
|
|