| Cr3+和Ni2+复合掺杂的尖晶石氧化物用于提高钻孔热电池放电性能 | |
| Cr3+ and Ni2+ Co-doped Spinel Oxide Cathode with Improved Capacity and Voltage Stability in Thermal Battery for Geothermal Borehole | |
| 摘要: 为了提高用于油气以及地热钻井热电池正极材料的比容量和电压稳定性，将Cr和Ni离子同时掺杂到尖晶石锰酸锂中。通过固相法制备的LiCrxNiyMn2-x-yO4（0 ≤ x ≤ 0.3，0 ≤ y ≤ 0.3）材料显示出结晶度良好的尖晶石相结构和规则的八面体形态。研究了LiCrxNiyMn2-x-yO4材料与LiNO3-KNO3共晶电解质的热相容性以及LiCrxNiyMn2-x-yO4/Li-Mg-B电池体系在10~30 mA·cm-2的电流密度以及200~300℃的温度范围内的放电性能。用Cr3+和Ni2+部分取代尖晶石中的锰，增强了尖晶石结构的稳定性，从而提高电池的电压和容量。其中，LiCr0.1Ni0.3Mn1.6O4在10 mA·cm-2和300℃的条件下具有最大比容量713.29 mAh·g-1，在LiNO3-KNO3熔盐电池中放电性能良好。 | |
| 关键词: 热电池 复合掺杂 尖晶石型锰酸锂 放电性能 钻孔应用 | |
| 基金项目: 国家自然科学基金（No.51774254，51774253，51701187，U1610123，51674226，51574207，51574206，51804279，51801189）和山西省科技重大专项（MC2016-06）资助 | |
| Abstract: In order to enhance specific capacity and voltage stability of cathode material for thermal battery used in oil/gas and geothermal boreholes, Cr and Ni ions were doped into spinel lithium manganate simultaneously. The LiCrxNiyMn2-x-yO4 (0 ≤ x ≤ 0.3, 0 ≤ y ≤ 0.3) material prepared by solid-state method showed a good purity of spinel phase and a regular octahedral crystalline particles morphology. We investigated the thermal compatibility of the LiCrxNiyMn2-x-yO4 material with LiNO3-KNO3 eutectic electrolyte and the discharge performance of LiCrxNiyMn2-x-yO4/Li-Mg-B battery system at current densities from 10 to 30 mA·cm-2 over a temperature range of 200 to 300℃. Partial substitution of Cr3+ and Ni2+ for Mn in spinel improved battery voltage and capacity due to the enhanced stability of spinel structure, and the LiCr0.1Ni0.3Mn1.6O4 had the maximal specific capacity of 713.29 mAh·g-1 at 10 mA·cm-2 at 300℃, showing great potential in LiNO3-KNO3 molten salt battery for geothermal borehole applications. | |
| Keywords: thermal battery co-doping spinel lithium manganate discharge performance borehole application | |
| 投稿时间：2018-12-03 修订日期：2019-03-28 | |
| 摘要点击次数: 1795 | |
| 全文下载次数: 1123 | |
| 宋恒旭,牛永强,赵宇宏,连冬晓,任敬霞,张妍妍,侯华.Cr3+和Ni2+复合掺杂的尖晶石氧化物用于提高钻孔热电池放电性能[J].无机化学学报,2019,35(5):915-922. | |
| 查看全文 查看/发表评论 下载PDF阅读器 | |
| Support information: | |
|
| |
|
| |
|
| |