| 单根锑掺杂ZnO微米线热电发电机的制备及热电性能 | |
| Fabrication and Characteristics of Thermoelectric Microgenerators Based on Single Sb Doped ZnO Microwire | |
| 摘要: 采用化学气相沉积（CVD）方法，在无催化剂的条件下，生长出了锑掺杂的超长、大尺寸ZnO微米线。测试表明微米线的平均长度可达1~2.5 cm，微米线中锑元素的含量约为3.1%（n/n）。此外，将挑选出的单根锑掺杂ZnO微米线以银浆为电极制作成热电发电机，并研究了微米线长度和微米线直径对器件输出性能的影响。研究表明当器件两电极之间的温差为20 K且两电极间微米线的长度为1.6 cm时，器件能够输出的最大电压和最大输出功率分别约为36 mV和10.8 nW，微米线的赛贝克系数约为-1.80 mV·K-1。此外，热电器件的输出电压随着微米线长度的增加而增大，随微米线直径的增加而减小。 | |
| 关键词: 化学气相沉积 锑掺杂 ZnO微米线 热电发电机 | |
| 基金项目: 国家自然科学基金（No.61574026，11405017）和辽宁省自然科学基金（No.201602453）资助项目。 | |
| Abstract: Large-scale Sb doped ZnO microwire arrays were grown by chemical vapor deposition method without using metal catalyst. The experimental results show that the length of the microwires is about 1~2.5 cm and the Sb concentration in microwires is about 3.1%(n/n). Moreover, thermoelectric generators were fabricated based on single Sb doped large-scale ZnO microwires. The influence of the length and diameter of microwires on the output characteristics of devices was investigated. Under a temperature difference of 20 K between two electrodes and the length of 1.6 cm, the devices can produce a maximum output voltage of about 36 mV, a maximum output power of about 10.8 nW. The single Sb-doped ZnO microwires show a Seebeck coefficient of about -1.80 mV·K-1. In addition, it is found that the output voltages of the thermoelectric device increase with the microwire length, and decrease with the microwire diameters. | |
| Keywords: chemical vapor deposition Sb doped ZnO microwires thermoelectric generators | |
| 投稿时间：2017-08-16 修订日期：2017-10-17 | |
| 摘要点击次数: 1649 | |
| 全文下载次数: 1269 | |
| 冯秋菊,石笑驰,邢研,李芳,李彤彤,潘德柱,梁红伟.单根锑掺杂ZnO微米线热电发电机的制备及热电性能[J].无机化学学报,2018,34(2):331-336. | |
| 查看全文 查看/发表评论 下载PDF阅读器 | |
| Support information: | |
|
| |
|
| |
|
| |