| Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate |
|
| 摘要: 在含有Ca2+，PO43-以及SiO32-的电解液中，通过电化学恒电位方法，在工作电压为3 V温度为85 ℃的条件下沉积1 h,于钛表面上制得含硅羟基磷灰石涂层。通过电感耦合等离子体原子发射光谱(ICP)、扫描电镜(SEM)、X-射线衍射(XRD)、探针式轮廓仪(SP)、红外光谱(FTIR)对涂层进行分析。结果表明：电化学恒电位方法可制得Si饱和含量为0.55wt%左右的Si-HA涂层，Si以SiO44-形式取代PO43-进入HA晶格，造成羟基磷灰石中OH-减小以维持电荷平衡。另外，电解液中Si元素的存在抑制涂层中HA晶体的生长，使涂层变薄，且当电解液中nSi/(nSi+nP)达到20%时Si-HA晶体形貌由单独的棒状转变为根部相连的树枝状。 |
| 关键词: 羟基磷灰石 硅掺杂 电化学沉积 涂层 |
| 基金项目: |
| Abstract: Silicon-substituted hydroxyapaptite coatings were prepared on titanium substrate with electrochemical deposition technique in electrolytes containing Ca2+, PO43- and SiO32- ions. The deposition was all conducted at a constant voltage of 3.0 V for 1 h at 85 ℃. The as-prepared coatings were examined by inductively coupled plasma(ICP), X-ray diffraction(XRD), stylus profiler(SP), Fourier transform infrared spectroscopy(FTIR), field-emission-type scanning electron microscope (SEM). The results show that the silicon amount in Si-HA coatings deposited by electrochemical method can reach to a saturation level of around 0.55wt%, and the substitution of silicate for phosphate in the form of SiO44- results in loss of some OH- to maintain the charge balance. Additionally, the presence of silicon ions in electrolytes inhibits HA crystals growth in coatings, leading to decrease of coating thickness and transformation of rod-like crystals into dendritic crystals in the electrolyte of 20% molar ratio silicon. |
| Keywords: hydroxyapatite silicon-substitution electrodeposition coating |
| |
| 摘要点击次数: 1696 |
| 全文下载次数: 2098 |
| 李登虎,林 军,林东洋,王小祥.钛表面含硅羟基磷灰石涂层的电化学合成和表征[J].无机化学学报,2011,27(6):1027-1032. |