| 纳米孔硅灰石载药抗菌止血材料的研究 |
| Hemostatic Agent of Nano Prorous Wollastonite Loaded Drug with Antibacterial Properties |
|
| 摘要: 采用溶胶-凝胶法，以聚氧乙烯-聚氧丙烯-聚氧乙烯三嵌段共聚物(P123)为模板剂，合成了纳米孔硅灰石(np-WT)，用np-WT载盐酸万古霉素研制了一种新型的载药抗菌止血材料，并对其止血性能进行了研究。结果表明：np-WT具有排列有序的纳米孔道结构，其孔径在2 nm左右，高比表面积的np-WT能够明显地缩短体外部分凝血活酶时间(APTT)和凝血酶原时间(PT)。载药np-WT能够在磷酸缓冲溶液(PBS)中缓慢地释放药物，载药np-WT对其凝血性能没有明显的影响。载药np-WT对大肠杆菌有很好的抗菌作用，细胞毒性实验表明：载药np-WT无细胞毒性。载药np-WT具有很好的止血性能，能够阻止兔背部伤口的流血和缩短其流血时间。 |
| 关键词: 纳米孔硅灰石 止血 药物缓释 抗菌 生物相容性 |
| 基金项目: |
| Abstract: A nanoprorous wollastonite (np-WT) was fabricated by using amphiphilic pluronic polymer surfactant (P123, EO20PO70EO20) as templates and sol-gel process, and a hemostatic agent of np-WT loaded drug (Vancomycin Hydrochloride) with antibacterial properties was investigated. The results showed that np-WT with large surface area and well ordered pores of around 2 nm could significantly shorten prothrombin time (PT) and the activated partial thromboplastin time (APTT). The np-WT loaded drug had no obvious effects on its hemostatic properties. The np-WT could slowly release drug into phosphate buffered saline(PBS) for 7 d. The np-WT loaded drug without cytotoxicity had good antibacterial properties. The np-WT loaded drug could shorten the bleeding time of rabbit back wound and control hemorrhage, showing good hemostatic properties. |
| Keywords: nanoprorous wollastonite hemostatic agent drug release antibacterial biocompatibility |
| |
| 摘要点击次数: 1434 |
| 全文下载次数: 2371 |
| 陈 于,徐 灿,苏佳灿,李文锐.纳米孔硅灰石载药抗菌止血材料的研究[J].无机化学学报,2011,27(4):625-630. |