| Ni-Fe/4A分子筛催化剂可控制备大内径碳纳米管 |
| Controlled Synthesis of Large Inner Diameter Carbon Nanotubes by Ni-Fe/Zeolite 4A Catalyst |
|
| 摘要: 以乙醇为碳源，Ni-Fe/4A分子筛为催化剂，采用化学气相沉积法制备大内径碳纳米管(LIDCNTs)。研究了Ni/Fe的物质的量比(nNi∶nFe)、碳纳米管(CNTs)的制备温度、催化剂的煅烧温度和4A分子筛载体对CNTs内径的影响。采用TEM、SEM、XRD和BET对LIDCNTs和还原后的催化剂进行了分析。结果显示，LIDCNTs的内径随着CNTs的制备温度、催化剂的煅烧温度的升高和nNi∶< |
| 关键词: 碳纳米管 大内径 CCVD Ni-Fe |
| 基金项目: |
| Abstract: Large inner diameter carbon nanotubes(LIDCNTs) were controlled prepared by chemical vapor deposition method using ethanol as carbon source and Ni-Fe/zeolite 4A as catalyst. The influences of Ni/Fe molar ratio(nNi∶nFe), carbon nanotubes(CNTs) preparation temperature, catalyst calcination temperature and zeolite 4A support on the inner diameter of CNTs were studied. The LIDCNTs and catalyst after reduction were investigated by TEM, SEM, XRD and BET. The results indicated that the inner diameter of LIDCNTs increased with the increasing of CNTs preparation temperature and catalyst calcination temperature, but decreased with the nNi∶nFe increasing. The inner diameter of CNTs can be controlled at 10～80 nm. |
| Keywords: carbon nanotubes large inner diameter CCVD Ni-Fe |
| |
| 摘要点击次数: 1612 |
| 全文下载次数: 1987 |
| 李国强,熊 亮,林浩强,瞿美臻.Ni-Fe/4A分子筛催化剂可控制备大内径碳纳米管[J].无机化学学报,2009,25(8):1330-1335. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|