| KIT-1介孔分子筛的化学修饰及吸附性能 |
| Chemical Modification and Adsorption of the Pure Silica Mesoporous Molecular Sieve KIT-1 |
|
| 摘要: |
| 关键词: 介孔分子筛 KIT-1 化学修饰 吸附容量 水热稳定性 |
| 基金项目: |
| Abstract: The pure silica mesoporous molecular sieve (KIT-1) was chemically modified using both organic and inorganic precursors and characterized using FTIR, XRD, MAS NMR, TG-DSC and physical adsorption-desorption of nitrogen. Experimental results showed that the original mesoporous structure of the samples remained after modification. The IR and MAS NMR spectra demonstrated that the organic groups (-Si(CH3)3 and -OCH2CH3) had successfully grafted onto the inter-surface of KIT-1 and inorganic atoms(Al, Si) attached at silicon atoms located in the hydrophobic part of the surface of KIT-1, but the grafted samples showed a lower BET surface area ,pore volume and smaller pore size. Modification using trimethylchlorosilane(TMCS) and TEOS was found to result in a significant loss in porosity. The surface property of samples was measured through adsorption capacity for the vapour of water or toluene. The modification samples show a higher adsorption capacity to toluene as compared to the parent KIT-1. The hydrophobicity of the sample modified by TMCS is much higher than other modified samples. Chemical modifications can greatly improve the hydrothermal stability of KIT-1 material because of the changed surface property. |
| Keywords: mesoporous molecular sieve KIT-1 chemical modification adsorption capacity. the hydrothermal stability |
| |
| 摘要点击次数: 1300 |
| 全文下载次数: 1896 |
| 李惠云,华伟明,何其戈,郭金福,乐英红.KIT-1介孔分子筛的化学修饰及吸附性能[J].无机化学学报,2007,23(6):1093-1098. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|