| 阴极材料LaFe0.8-xCuxNi0.2O3的合成和烧结性能 |
| Synthesis and Sintering of Cathode Materials LaFe0.8-xCuxNi0.2O3 |
|
| 摘要: |
| 关键词: 阴极材料 LaFe0.8-xCuxNi0.2O3 共沉淀法 烧结性能 |
| 基金项目: |
| Abstract: LaFe0.8-xCuxNi0.2O3 (x=0.0~0.2) (LFCN), a new cathode material of solid oxide fuel cell (SOFC), was synthesized by Co-precipitation method using sodium bicarbonate. The lattice structures of samples with different x contents were characterized by XRD. Porosity and density of the porous LaFe0.8-xCuxNi0.2O3 (x=0.0~0.1) as a function of sintering temperature were investigated. It was found that the orthorhombic structure could be formed after calcination at 900 ℃ for 4 h. The particle size of LFCN was about 350 nm. The density of the porous LFCN increased with sintering temperature, but the opposite was true for the porosity. On the other hand, at the same sintering temperature, the porosity of LaFe0.8-xCuxNi0.2O3 (x=0.0~0.1) decreased with increasing x contents. It is indicated that the dopant of Cu on LaFe0.8Ni0.2O3 can facilitate the sintering of the materials. After sintering at 1 100 ℃ for 4 h, the porous LaFe0.7Cu0.1Ni0.2O3 was still with appropriate structure, and its porosity was 29%. |
| Keywords: cathode material LaFe0.8-xCuxNi0.2O3 Co-precipitation method sintering |
| |
| 摘要点击次数: 1730 |
| 全文下载次数: 1957 |
| 李嵩,文钟晟,季世军,孙俊才,程成.阴极材料LaFe0.8-xCuxNi0.2O3的合成和烧结性能[J].无机化学学报,2006,22(1):149-152. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|