| 硫酸/草酸混酸电解液中阳极氧化法制备多孔阳极氧化铝模板 |
| Preparation of Porous Anodic Alumina Templates Using a Sulfuric / Oxalic Acid Mixture as Electrolyte |
|
| 摘要: |
| 关键词: 阳极氧化 多孔氧化铝 纳米材料 |
| 基金项目: |
| Abstract: Well ordered porous anodic alumina (PAA) film was prepared on pure Al substrate using sulfuric/oxalic acid mixture as electrolyte with different ratios, the best regular PAA film with an average diameter of 45 nm was obtained using 1∶1 sulfuric/oxalic (molar concentration) mixed acid at 26 V. Addition of oxalic acid into sulfuric acid electrolyte resulted in the increase of anodizing current density, indicating a faster formation rate of PAA film. In 1∶1 sulfuric/oxalic acid electrolyte, the current density was the biggest, which illustrated that the formed barrier layer was the thinnest. Besides, addition of oxalic acid increased the stress of oxide film, accordingly changed the self-organized process of PAA film. XPS results indicate that the PAA film is mainly composed of amorphous alumina independent of oxalic acid addition. |
| Keywords: anodization porous anodic alumina nano-materials |
| 投稿时间：2005-05-30 修订日期：2005-08-17 |
| 摘要点击次数: 1304 |
| 全文下载次数: 3831 |
| 杨培霞,安茂忠,郑铁帅.硫酸/草酸混酸电解液中阳极氧化法制备多孔阳极氧化铝模板[J].无机化学学报,2005,21(12):1907-1911. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|