| Ce0.8Y0.2O1.9-Ca3(PO4)2-K3PO4复合电解质在中温区的质子导电性及在常压合成氨中的应用 |
| Doped Ceria-Ca3(PO4)2-K3PO4 Composite Electrolyte: Proton Conductivity at Intermediate Temperature and Application in Atmospheric Pressure Ammonia Synthesis |
|
| 摘要: |
| 关键词: 复合电解质 离子电导率 常压合成氨 YDC |
| 基金项目: |
| Abstract: A precursor of Ce0.8Y0.2O1.9(YDC) solid electrolyte was synthesized by the gol-gel method. YDC and phosphates powders were prepared by mixing the YDC and phosphates according to different weight ratios. The mixtures of the YDC and binary phosphates were ground and sintered at 1 400 ℃. The proton conductivity in solid electrolyte of the sintered samples was examined using electrochemical methods at 400～800 ℃. Ammonia was synthesized from nitrogen and hydrogen at atmospheric pressure in the solid state proton conducting cell reactor. The optimal condition for the ammonia production was determined. The result indicated that composite electrolyte of 80wt% YDC: 20wt% binary phosphates as proton conductor could obtain the highest ionic conductivity and ammonia production rate among the four samples, the rate of evolution of ammonia was up to 9.5 × 10-9 mol·s-1·cm-2. |
| Keywords: composite electrolyte ionic conductivity ammonia synthesis at atmospheric pressure YDC |
| 投稿时间：2005-03-06 修订日期：2005-06-22 |
| 摘要点击次数: 3863 |
| 全文下载次数: 1688 |
| 王本辉,刘瑞泉,王吉德,李志杰,谢亚红.Ce0.8Y0.2O1.9-Ca3(PO4)2-K3PO4复合电解质在中温区的质子导电性及在常压合成氨中的应用[J].无机化学学报,2005,21(10):1551-1555. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|