| 从P-Mo(Ⅴ)杂多化合物合成多形貌Al13基钼酸盐晶体 |
| Al13 Based Molybdate Crystals with Multimorphologies Synthesized from P-Mo(Ⅴ) Heteropoly Compounds |
|
| 摘要: 以H3PMo12O40·nH2O、H4PMo11VO40·nH2O和(NH4)6P2Mo18O62·nH2O 3种杂多化合物为钼源，采用直接混合后陈化的方法合成了多形貌Al13基钼酸盐晶体，相应Al13基钼酸盐晶体的形貌和尺寸分别是斜方三棱柱形(80 μm × 30 μm)、星形(30 μm × 10 μm)和叶片形(500 μm × 150 μm)。粉末X射线衍射结果表明这3种多形貌Al13基钼酸盐晶体结晶较好，在2θ为6.65°、8.00°和14.16°处都有强而尖锐的衍射峰。而以Na2MoO4·2H2O为钼源时只能制得无定形簇合物。根据ICP、FTIR和TG/DTG结果给出多形貌的Al13基钼酸盐晶体的化学简式为Na[AlO4Al12(OH)24(H2O)12][MoO4]4·8H2O。初步探讨了Al13基钼酸盐晶体的形成机理。 |
| 关键词: Al13聚离子 杂多化合物 钼酸盐晶体 晶体生长 |
| 基金项目: |
| Abstract: The Al13 based molybdate crystals with multimorphologies were synthesized via a direct mixing and aging method. The heteropoly compounds of H3PMo12O40·nH2O、H4PMo11VO40·nH2O and (NH4)6P2Mo18O62·nH2O (abbr. P-Mo(Ⅴ) heteropoly compounds) were employed as the molybdate sources. The corresponding morphology and size of the molybdate crystals is trimetrical-prismy like (80 μm × 30 μm), star-like (30 μm × 10 μm) and leaf-like (500 μm × 150 μm). XRD patterns show that the Al13 based molybdates with multimorphologies are of high crystallinity, and have strong and sharp peaks (2θ) at 6.65°, 8.00° and 14.16°. However, when Na2MoO4·2H2O was used, there were only amorphous clusters in a similar process. According to the results of ICP, FTIR and TG / DTG, the chemical formula of the Al13 based molybdate crystals is Na[AlO4Al12(OH)24(H2O)12][MoO4]4·8H2O. The probable crystal growth mechanism is proposed. |
| Keywords: Al13 polyoxocations heteropoly compounds molybdate crystals crystal growth |
| 投稿时间：2004-07-08 修订日期：2005-01-23 |
| 摘要点击次数: 1449 |
| 全文下载次数: 2109 |
| 张渊明,杨发达,李红,唐渝,杨骏.从P-Mo(Ⅴ)杂多化合物合成多形貌Al13基钼酸盐晶体[J].无机化学学报,2005,21(5):626-632. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|