| Abstract: The nanometer TiO2 were prepared by the hydrolyze-gel method and fellowed by doping alkaline-earth metals (Mg, Ca, Sr, Ba). XRD, SEM, diffuse reflection spectra were used to investigate their characteristices. The result indicates that the average particles size of the TiO2 is about 80 nm and keep uniformity in distributing. The product was mainly anatase in 300～400 ℃ calcinations, the einstein shift of absorption spectrum was observed after doping the alkaline-earth metals. The best mole percentages of Mg, Ca, Sr and Ba are 0.5%, 1.0%, 1.5%, 1.5% respectively. Under the same reaction conditions, it is more effective to the UV-catalyed degradation reaction that the catalysts containing Mg and Ca were calcined at 300 ℃ for 1h or containing Sr and Ba were calcined at 400 ℃ for 1 h. The photocatalystic activity is considerably depondent on pH and the concentration of the oxidant. Using the sunlight to do the degradation experimental, the result also show that the doping catalysts has higher degradation efficiency than that of pure TiO2. |