| 用于制备聚氨酯纳米复合物的高岭石粒子的表征(英文) | |
| Characterization of Nano Kaolinite Clay used in Polyurethane Composite | |
| 摘要: | |
| 关键词: 高岭石粒子 表征 纳米复合聚合物 | |
| 基金项目: | |
| Abstract: Clay such as kaolinite， is commonly used as an additive to modify the thermal properties of polymer. In this paper， the morphology， composition， shape and structure of kaolinite was characterized by various advanced techniques. The TEM/ EDX data showed that the kaolinite had a larger particle size and a Si/Al ratio of 1.8. The individual particle of kaolinite was a single crystalline. TEM also showed that these particles were always stacked together due to the presence of electrostatic cohesive energy and hydrogen bond between plaletes. The PAS-FTIR spectra showed that no absorbance of hydroxyl group for hydration water in hydrogen bond region or at 1650cm-1 was observed at room temperature. It meant a little ability to adsorb water for kaolinite particle. Kaolinite clay also showed no change for its PAS-FTIR spectra with increasing temperature. The TGA results revealed that kaolinite almost doesn′t lose weight at 60℃ due to loss of dehydration of absorbed water， however， it will decomposed around 510℃ and lose its hydroxyl functional group in the form of water (dehydroxylation). The result is consistent with that of PAS-FTIR analysis. This suggests that the structural hydroxyl group on the surface of individual kaolinite clay particle is very stable below 500℃， and the kaolinite composed polymer could be got by the reaction of its stable structural hydroxyl group with isocynate group of polyurethane prepolymer. | |
| Keywords: kaolinite clay characterization nano composite polymer | |
| 摘要点击次数: 1377 | |
| 全文下载次数: 1350 | |
| 李再峰,王义银,Luba S. Kotlyar,Keng H. Chung.用于制备聚氨酯纳米复合物的高岭石粒子的表征(英文)[J].无机化学学报,2003,19(11):1261-1265. | |
| 查看全文 查看/发表评论 下载PDF阅读器 | |
| Support information: | |
|
| |
|
| |
|
| |