| 纳米晶SnO2粉体的合成 |
| Synthesis of Crystalline Tin Oxide Nanopowders |
|
| 摘要: |
| 关键词: 纳米粉体 SnO2 合成 |
| 基金项目: |
| Abstract: Crystalline tin oxide nanoparticles were synthesized by the direct precipitation from the starting material granulated tin. TG-DTA of the precursor showed a heavy weight loss at about 130℃ accompanied by an endothermic peak， two exothermic peaks above 200℃ accompanied by small weight loss indicated the decomposition and the oxidation of residual NO3- ion and PEG. XRD showed that obtained particles agreed well with the determination result of bulk SnO2. The broadened XRD patterns became sharper as the calcining temperature turned to higher， it was indicated that the growth of the particle was exhibited. The surface area of the particles calcined at 300℃ was 161.1m2·g-1 and declined as the calcining temperature turned to higher. TEM showed an heavier agglomeration at higher temperature. |
| Keywords: nanopowder SnO2 synthesis |
| |
| 摘要点击次数: 1644 |
| 全文下载次数: 2081 |
| 张建荣,高濂.纳米晶SnO2粉体的合成[J].无机化学学报,2003,19(6):641-644. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|