| 二氧化硅改性片状铁粒子的微波吸收性能 |
| Microwave-Absorbing Behavior of Silica-Modified Platelet Iron Particles |
|
| 摘要: |
| 关键词: 片状铁粒子 微波吸收性能 水热反应 二氧化硅改性 |
| 基金项目: |
| Abstract: The preparation and microwave-absorbing behavior of micrometric silica-modified platelet iron particles (SMPLIP) were investigated. Through precipitation， hydrothermal reaction， silica-modification and reduction with hydrogen， micrometric porous SMPLIP were yielded. The permittivity values of SMPLIP had been significantly decreased due to the presence of silica. Measurements and calculations showed that a 1.93mm thick sample containing SMPLIP as much as 60% by weight was capable of absorbing X band(8.2～12.4GHz) microwaves with reflection loss being greater than -10dB within the frequency range of 8.2～11.36GHz， while the maximum re-flection loss was -14.8dB at 9.4GHz. The results had also shown that it was practicable to prepare thin， light-weight microwave absorbent with SMPLIP. |
| Keywords: platelet iron particles microwave-absorbing behavior hydrothermal reaction silica modification |
| |
| 摘要点击次数: 1219 |
| 全文下载次数: 2126 |
| 孟凡君,茹淼焱,刘爱祥,刘宗林.二氧化硅改性片状铁粒子的微波吸收性能[J].无机化学学报,2003,19(2):211-214. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|