| Li2+2xZn1-xSiO4水基溶胶-凝胶法合成及其离子导电性 |
| Synthesis of Li2+2xZn1-xSiO4 by Water-Based Sol-Gel Method and Its Ionic Conductivity |
|
| 摘要: 用水基溶胶凝胶法制备了锂离子导体Li2+2xZn1-xSiO4(0≤x≤0.5)。实验中对干凝胶的热稳定性进行了TG-DTG分析。XRD谱结果表明形成了与Li3PO4结构相关的固溶体Li2+2xZn1-xSiO4。TEM结果则显示晶粒尺寸为50nm左右,并应用交流阻抗谱技术进行了样品烧结体的电性能测试。 |
| 关键词: 正硅酸锂锌固溶体 离子导电性 水基溶胶-凝胶法 |
| 基金项目: 河北省自然科学基金资助项目(No.296169) |
| Abstract: A liquid source using water as a solvent was studied to prepare Li2+2xZn1-xSiO4 single phase by a Sol Gel method. XRD results show that the solid solution Li2+2xZn1-xSiO4 (0≤x≤0.5) is structurally related to Li3PO4 phase. TEM photographs show that the grain size of the sample annealed at 900℃ is about 50nm. Ionic conductivity was determined by means of A Cimpedance technique. Compared with the samples by the conventional solid state reaction, the experimental results shows that Li2+2xZn1-xSiO4 can be obtained using by water based sol gel method at lower temperature. |
| Keywords: lithium zinc silicate ionic conductivity water-based sol-gel method |
| 投稿时间：1999-04-01 修订日期：1999-06-30 |
| 摘要点击次数: 1405 |
| 全文下载次数: 2036 |
| 宋秀芹,陈汝芬,马建峰.Li2+2xZn1-xSiO4水基溶胶-凝胶法合成及其离子导电性[J].无机化学学报,2000,16(1):37-42. |
| 查看全文 查看/发表评论 下载PDF阅读器 |
| Support information: |
|
|
|
|
|
|